| Summary: | This paper presets the results of the comparative investigation of structure, phase composition, mechanical and magnetic properties of the bimetal materials produced by means of explosion welding. The base metal is represented by high-strength hull steel and the cladding layer — by two corrosion-resistant steel with different stability of austenite. Investigations of structure and phase composition were carried out. According to the results of the shear tests, it has been shown that explosion welding provides a strength joint with high values of the bond strength of the layers. Informative magnetic parameters, allowing evaluating the changes occurring in individual layers of bimetal corrosion-resistant materials during plastic deformation were detected. В работе представлены результаты сравнительного исследования структуры, механических и магнитных свойств биметаллических материалов, полученных по технологии сварки взрывом. Основной слой — это корпусная высокопрочная сталь, плакирование выполнялось двумя коррозионностойкими сталями с разной степенью стабильности аустенита. Проведены исследования структуры и фазового состава. Результаты испытания на срез показали, что сварка взрывом позволяет получить прочное неразъемное соединение с высокими значениями прочности соединения слоев. Установлены информативные магнитные параметры, позволяющие оценивать изменения, происходящие в отдельных слоях биметаллических коррозионностойких материалов при пластическом деформировании. Работа выполнена при частичной поддержке гранта РФФИ 16-38-60027‑мол_а_дк. При выполнении работы использовано оборудование ЦКП «Пластометрия».
|
|---|