Enzyme-catalysed polymerization and degradation of copolyesters of e-caprolactone and g-butyrolactone
International audience Copolymers of g-butyrolactone (g-BL) and 3-caprolactone (3-CL) were successfully synthesized by ring-opening polymerization using Novozyme-435 (immobilized lipase B from Candida antartica) as catalyst. Copolymers with different compositions were obtained and characterized by 1...
Published in: | Polymer |
---|---|
Main Author: | |
Other Authors: | , , |
Format: | Article in Journal/Newspaper |
Language: | English |
Published: |
HAL CCSD
2005
|
Subjects: | |
Online Access: | https://hal.science/hal-00417160 https://doi.org/10.1016/j.polymer.2005.10.121 |
Summary: | International audience Copolymers of g-butyrolactone (g-BL) and 3-caprolactone (3-CL) were successfully synthesized by ring-opening polymerization using Novozyme-435 (immobilized lipase B from Candida antartica) as catalyst. Copolymers with different compositions were obtained and characterized by 1H NMR, 13C NMR, GPC, DSC and X-ray diffraction. Increasing the [BL]/[CL] feed ratio resulted in decreases of molecular weight (Mn) of copolymers and reaction yield. Moreover, the BL contents in the copolymers varied according to the feed ratio. The Tm of the copolymers decreased from 58 to 49 8C with increase in BL content from 0 to 14%. The resulting copolymers were all semicrystalline with a PCLtype crystalline structure. Solution cast films were allowed to degrade in a pH 7.0 phosphate buffer solution containing Pseudomonas lipase. Weight loss data showed that the degradation rate of copolymers in the presence of Pseudomonas lipase decreased with the increase of BL contents. |
---|