| Summary: | Thesis (M.S.) University of Alaska Fairbanks, 2014 The purpose of this research work was to study the beneficiation of rare earth ore of the Bokan Mountain -- Dotson Ridge deposit, located near Ketchikan, Alaska. Rare earth element (REE) composite ore samples from the Bokan Mountain -- Dotson Ridge deposit were tested using gravity concentration, magnetic separation, flotation, and leaching techniques to separate the REE. The composite ore sample was a product of a preliminary x-ray sorting process. Qualitative electron microprobe analysis of the ore showed that most of the REE minerals in the ore were silicate minerals. Since the electron microprobe analysis samples were coated with carbon during sample preparation, the carbon element was inactivated for analysis. Because of this, carbonate compounds of minerals' particles could not be detected. 95% of the REE mineral particles appear to be smaller than about 10 μm in size (about 100 μm² in area). For the gravity concentration, light rare earth elements (LREE) and heavy rare earth elements' (HREE) individual elemental recovery values were in the ranges of 49.6-52.8% and 46.3-48.8%, respectively, at 25% of mass yield. In order to separate a larger amount of the REE, a wet high intensity magnetic separation (WHIMS) test was carried out on tailings of the gravity concentration tests. The HREE individual elemental recovery values ranged from 56.3-63.1% at 37% mass yield, while LREE individual elemental recovery values were in the 57.9% - 59.1% range. For the combined gravity and magnetic separation processes, the net individual elemental recovery values of the LREE and the HREE were in the range of 79.6-80.5% and 76.5-80.9%, respectively. The combined mass yield of the gravity and magnetic separation processes was 3%. Direct leaching tests conducted on the composite ground ore feed yielded high individual elemental recovery values of 90-92% of the LREE. The HREE individual elemental recovery values ranged from 56.5-87.3%. In the leaching, 20% HCl was used in the ...
|
|---|