Room Temperature Corrosion Behavior of Selective Laser Melting (SLM)-Processed Ni-Fe Superalloy (Inconel 718) in 3.5% NaCl Solution at Different pH Conditions: Role of Microstructures

Inconel 718 (UNS N07718) is a nickel-base superalloy containing iron that is used at cryogenic temperatures (arctic pipe components) and at high temperatures (gas turbines). This alloy is also used in off-shore oil drilling due to its high overall strength and resistance to corrosion. Inconel 718 co...

Full description

Bibliographic Details
Published in:Crystals
Main Authors: Thomas Thuneman, Krishnan S. Raja, Indrajit Charit
Format: Article in Journal/Newspaper
Language:English
Published: MDPI AG 2024
Subjects:
Online Access:https://doi.org/10.3390/cryst14010089
https://doaj.org/article/9705ca4700714b0fa87290f6d196d37e
Description
Summary:Inconel 718 (UNS N07718) is a nickel-base superalloy containing iron that is used at cryogenic temperatures (arctic pipe components) and at high temperatures (gas turbines). This alloy is also used in off-shore oil drilling due to its high overall strength and resistance to corrosion. Inconel 718 components are created by a selective laser melting (SLM) additive manufacturing route and result in isotropic fine-grained microstructures with metastable phases (such as Laves phases) that are not usually present in conventional manufacturing processes. In this work, SLM Inconel 718 alloy specimens were investigated in four different conditions: (1) As-manufactured (AS-AM), (2) Additively manufactured and hot isostatically pressed (AM-HIP), (3) As-manufactured and heat-treated (solution annealing followed by two-step aging), and 4) AM-HIP and heat-treated. Localized corrosion behavior was evaluated at room temperature in a 3.5% NaCl solution at three different pH conditions (pH 1.25, 6.25, and 12.25). Electrochemical tests, including linear polarization, cyclic polarization, potentiostatic conditioning, electrochemical impedance spectroscopy, and Mott–Schottky analyses, were used to compare the corrosion behaviors of the SLM specimens with that of the conventionally wrought IN718 samples. The results showed that the additively manufactured specimens showed better corrosion resistance than the wrought material in the acidic chloride solution, and the AM-HIP specimens exhibited superior corrosion resistance to the as-manufactured ones. Hot isostatic pressing resulted in the visible elimination of the dendritic structure, indicating compositional homogeneity as well as a significant decrease in porosity. In addition, the deleterious secondary phases, such as Laves and δ phases, were not observed in the microstructure of the HIPed samples. The AM-HIP material showed the highest corrosion resistance in all the pH conditions. The two-step aging treatment, in general, resulted in the deterioration of corrosion resistance, ...