Ice triaxial deformation and fracture
Abstract An experimental investigation into the mechanical behaviour of polycrystalline ice in triaxial compression has been conducted using conditions generally favourable to brittle fracture and microcracking. Under triaxial stresses at high strain rate, ice failure occurs by abrupt shear fracturi...
| Published in: | Journal of Glaciology |
|---|---|
| Main Authors: | , |
| Format: | Article in Journal/Newspaper |
| Language: | English |
| Published: |
Cambridge University Press (CUP)
1994
|
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1017/s0022143000007395 https://www.cambridge.org/core/services/aop-cambridge-core/content/view/S0022143000007395 |
| Summary: | Abstract An experimental investigation into the mechanical behaviour of polycrystalline ice in triaxial compression has been conducted using conditions generally favourable to brittle fracture and microcracking. Under triaxial stresses at high strain rate, ice failure occurs by abrupt shear fracturing, generally inclined at about 45° to the maximum principal stress. At −20°C, such failure is suppressed by the imposition of a small confining pressure, allowing a transition to ductile-type flow accompanied by distributed microcracking, but at —40°C shear fracture persists under confinement of up to at least 50 MPa. For low confining pressures (< 10 MPa), brittle strength is strongly pressure-dependent; above this it is pressure-independent. Evidence is presented that suggests this may reflect a change from a fracture process influenced by friction to fracture initiated by localized yielding. Ductile yield strength is found to be little influenced by confining pressure despite the inhibition of cracking that leads to greatly contrasting observed crack densities. Flow conforms to the well-known power law for ice with Q = 69 J mol −1 and n = 4.2 over the temperature range −20° to −4-5° C Under these conditions, microcracking in ice appears to remain remarkably stable and non-interacting. |
|---|