Selective paint development. Technical progress report, 5 December 1978-31 July 1979
Eighteen hundred square feet of aluminum foil were coated with thickness-sensitive selective paint. The feasibility of a high speed, large-scale roller coating technique was demonstrated. Coating thermal stability, weathering and humidity resistance, and effects of pigment particle size on coating o...
Main Authors: | , , |
---|---|
Language: | unknown |
Published: |
2013
|
Subjects: | |
Online Access: | http://www.osti.gov/servlets/purl/5515391 https://www.osti.gov/biblio/5515391 https://doi.org/10.2172/5515391 |
id |
ftosti:oai:osti.gov:5515391 |
---|---|
record_format |
openpolar |
spelling |
ftosti:oai:osti.gov:5515391 2023-07-30T04:02:55+02:00 Selective paint development. Technical progress report, 5 December 1978-31 July 1979 McKelvey, W D Zimmer, P B Lin, R J.H. 2013-06-13 application/pdf http://www.osti.gov/servlets/purl/5515391 https://www.osti.gov/biblio/5515391 https://doi.org/10.2172/5515391 unknown http://www.osti.gov/servlets/purl/5515391 https://www.osti.gov/biblio/5515391 https://doi.org/10.2172/5515391 doi:10.2172/5515391 14 SOLAR ENERGY ALUMINIUM COATINGS PAINTS OPTICAL PROPERTIES SURFACE COATING SPECTRALLY SELECTIVE SURFACES CHROMIUM OXIDES FOILS STABILITY URETHANE WEATHERING CARBAMATES CARBONIC ACID DERIVATIVES CARBOXYLIC ACID SALTS CHALCOGENIDES CHROMIUM COMPOUNDS DEPOSITION ELEMENTS EQUIPMENT METALS ORGANIC COMPOUNDS ORGANIC NITROGEN COMPOUNDS OXIDES OXYGEN COMPOUNDS PHYSICAL PROPERTIES SOLAR EQUIPMENT SURFACES TRANSITION ELEMENT COMPOUNDS 2013 ftosti https://doi.org/10.2172/5515391 2023-07-11T10:40:23Z Eighteen hundred square feet of aluminum foil were coated with thickness-sensitive selective paint. The feasibility of a high speed, large-scale roller coating technique was demonstrated. Coating thermal stability, weathering and humidity resistance, and effects of pigment particle size on coating optical properties were studied. Thickness-insensitive paint with urethane binder was evaluated. A medium scale (1 kg) of thickness-insensitive paint solution was prepared which achieved an .cap alpha./sub s/ of 0.90 and epsilon of 0.35. Other/Unknown Material Carbonic acid SciTec Connect (Office of Scientific and Technical Information - OSTI, U.S. Department of Energy) |
institution |
Open Polar |
collection |
SciTec Connect (Office of Scientific and Technical Information - OSTI, U.S. Department of Energy) |
op_collection_id |
ftosti |
language |
unknown |
topic |
14 SOLAR ENERGY ALUMINIUM COATINGS PAINTS OPTICAL PROPERTIES SURFACE COATING SPECTRALLY SELECTIVE SURFACES CHROMIUM OXIDES FOILS STABILITY URETHANE WEATHERING CARBAMATES CARBONIC ACID DERIVATIVES CARBOXYLIC ACID SALTS CHALCOGENIDES CHROMIUM COMPOUNDS DEPOSITION ELEMENTS EQUIPMENT METALS ORGANIC COMPOUNDS ORGANIC NITROGEN COMPOUNDS OXIDES OXYGEN COMPOUNDS PHYSICAL PROPERTIES SOLAR EQUIPMENT SURFACES TRANSITION ELEMENT COMPOUNDS |
spellingShingle |
14 SOLAR ENERGY ALUMINIUM COATINGS PAINTS OPTICAL PROPERTIES SURFACE COATING SPECTRALLY SELECTIVE SURFACES CHROMIUM OXIDES FOILS STABILITY URETHANE WEATHERING CARBAMATES CARBONIC ACID DERIVATIVES CARBOXYLIC ACID SALTS CHALCOGENIDES CHROMIUM COMPOUNDS DEPOSITION ELEMENTS EQUIPMENT METALS ORGANIC COMPOUNDS ORGANIC NITROGEN COMPOUNDS OXIDES OXYGEN COMPOUNDS PHYSICAL PROPERTIES SOLAR EQUIPMENT SURFACES TRANSITION ELEMENT COMPOUNDS McKelvey, W D Zimmer, P B Lin, R J.H. Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
topic_facet |
14 SOLAR ENERGY ALUMINIUM COATINGS PAINTS OPTICAL PROPERTIES SURFACE COATING SPECTRALLY SELECTIVE SURFACES CHROMIUM OXIDES FOILS STABILITY URETHANE WEATHERING CARBAMATES CARBONIC ACID DERIVATIVES CARBOXYLIC ACID SALTS CHALCOGENIDES CHROMIUM COMPOUNDS DEPOSITION ELEMENTS EQUIPMENT METALS ORGANIC COMPOUNDS ORGANIC NITROGEN COMPOUNDS OXIDES OXYGEN COMPOUNDS PHYSICAL PROPERTIES SOLAR EQUIPMENT SURFACES TRANSITION ELEMENT COMPOUNDS |
description |
Eighteen hundred square feet of aluminum foil were coated with thickness-sensitive selective paint. The feasibility of a high speed, large-scale roller coating technique was demonstrated. Coating thermal stability, weathering and humidity resistance, and effects of pigment particle size on coating optical properties were studied. Thickness-insensitive paint with urethane binder was evaluated. A medium scale (1 kg) of thickness-insensitive paint solution was prepared which achieved an .cap alpha./sub s/ of 0.90 and epsilon of 0.35. |
author |
McKelvey, W D Zimmer, P B Lin, R J.H. |
author_facet |
McKelvey, W D Zimmer, P B Lin, R J.H. |
author_sort |
McKelvey, W D |
title |
Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
title_short |
Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
title_full |
Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
title_fullStr |
Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
title_full_unstemmed |
Selective paint development. Technical progress report, 5 December 1978-31 July 1979 |
title_sort |
selective paint development. technical progress report, 5 december 1978-31 july 1979 |
publishDate |
2013 |
url |
http://www.osti.gov/servlets/purl/5515391 https://www.osti.gov/biblio/5515391 https://doi.org/10.2172/5515391 |
genre |
Carbonic acid |
genre_facet |
Carbonic acid |
op_relation |
http://www.osti.gov/servlets/purl/5515391 https://www.osti.gov/biblio/5515391 https://doi.org/10.2172/5515391 doi:10.2172/5515391 |
op_doi |
https://doi.org/10.2172/5515391 |
_version_ |
1772813792256720896 |